RUMEX

	AquaFree Yellow Aspheric Hydrophobic	AquaFree Yellow Preloaded
	Instruction for use	Instruction for use
Min.incision size	2.20 mm	2.20 mm
Overall diameter	13.00 mm	13.00 mm
Optic diameter	6.00 mm	6.00 mm
Power range	0D to +9D (1D steps) +10D to +30D (0.5D steps)	0D to +9D (1D steps) +10D to +30D (0.5D steps)
Self-unfolding	Yes	Yes
Water content	< 0.50 %	< 0.50 %
Angulation	0°	0°
Material	Natural Yellow Hydrophobic Acrylic	Natural Yellow Hydrophobic Acrylic
Optic design	Biconvex, square-edge	Biconvex, square-edge
Refractive index	1.50	1.50
Abbe number	50	50
Nominal A-constant	118.7	118.7
Optimized optical constants	Haigis: a0=1.32, a1=0.40, a2=0.10 Hoff erQ: pAcD=5.51 Holl.1: sf=1.75 SRK/T: 118.9 SRK ii: 119.2 n: 190 Ref. : [304],[332]	Haigis: a0=1.32, a1=0.40, a2=0.10 Hoff erQ: pAcD=5.51 Holl.1: sf=1.75 SRK/T: 118.9 SRK ii: 119.2 n: 190 Ref. : [304],[332]
Transition temperature of material	11°C	11°C
Filtration	UV and blue light (400-475 nm)	UV and blue light (400-475 nm)
AC-depth	5.51	5.51
Shelf life	5 years	5 years

AquaFree Yellow Aspheric Hydrophobic

AquaFree Yellow Preloaded

Instruction for use

Min.incision size

2.20 mm

Overall diameter

13.00 mm

Optic diameter

6.00 mm

Power range

0D to +9D (1D steps)
+10D to +30D (0.5D steps)

Self-unfolding

Yes

Water content

< 0.50 %

Angulation

0°

Material

Natural Yellow Hydrophobic Acrylic

Optic design

Biconvex, square-edge

Refractive index

1.50

Abbe number

Nominal A-constant

118.7

Optimized optical constants

Haigis: a0=1.32, a1=0.40, a2=0.10
Hoff erQ: pAcD=5.51
Holl.1: sf=1.75
SRK/T: 118.9
SRK ii: 119.2
n: 190
Ref. : [304],[332]

Transition temperature of material

11°C

Filtration

UV and blue light (400-475 nm)

AC-depth

5.51

Shelf life

5 years

Low chromatic aberration – increased contrast sensitivity, excellent color perception
UV and blue light blocking – better protection of Macula
Extreme double square-edge – no risk of secondary cataract development
No spherical aberrations – minimized glare and unwanted images
mplantation through a 2.2 mm incision – fast recovery
Cryo-lathing method of manufacturing – no glistening

Special surface polishing – a lens does not stick to itself or instruments
Low glass transition temperature – excellent material performance in operating conditions
Optimal folding and unfolding ability – easy to inject
Preloaded option available – simple and predictable iol injection within less than 5 seconds